Effect of liquid medium and laser processing parameters on the fabrication of carbon nanoparticles via pulsed laser ablation in liquid towards paper electronics

https://doi.org/10.1016/j.colsurfa.2021.128151Get rights and content
Under a Creative Commons license
open access

Highlights

  • This paper studies the effect of liquid medium on nanoparticle mean size during Pulsed Laser Ablation in Liquid (PLAL).

  • A complex liquid medium (magnesium-based solution) is used for the first time during PLAL of carbon targets.

  • The effect of laser scan speed and fluence on the nanoparticle size and conductivity is investigated.

Abstract

Paper-based electronics with carbon nanomaterials incorporated have several advantages including recyclability, biodegradability, non-toxicity, low cost and ease of fabrication and disposal. Herein, carbon nanoparticles (CNPs) were fabricated by Pulsed Laser Ablation in Liquid (PLAL) using three different liquid mediums, i.e. deionised (DI) water, ethanol and a magnesium-based solution. The as-fabricated nanocolloids were used as conductive inks and deposited on paper substrates. The resulting nanoparticle (NP) coatings were subjected to electrical resistivity tests via 4-point probe. Ultraviolet–Visible spectroscopy (UV–Vis) studies were conducted to determine the presence of nanomaterials. All nanocolloids produced within DI water had three distinct UV–Vis absorbance peaks at 200, 216 and 225 nm while nanocolloids produced in ethanol exhibited more peaks and significantly higher absorbance values in the range from 210 nm to 300 nm. Dynamic Light Scattering and field emission scanning electron microscopy (FESEM) were used to analyse samples for particle size and morphology respectively. The liquid medium in which PLAL was conducted was found to significantly affect the NP mean size, conductivity and surface chemistry of the resulting NPs. DI water produced smaller nanoparticles (NPs) (10–82 nm) than ethanol (60–143 nm) and magnesium-based solution (263–1389 nm) within the process parameters studied herein. The laser scan speed and fluence have a combined effect on the NP mean diameter. The surface chemistry of the NPs produced in the magnesium-based solution was analysed via X-ray photoelectron spectroscopy and it was found that the Mg, Li and Si atoms are adsorbed by the carbon NPs leading to higher conductivity of the coated paper substrates.

Keywords

Paper electronics
Conductive inks
Pulsed laser ablation in liquid
Carbon nanoparticles
Drop casting
Nanoinks
Additive manufacturing